ML 5554 AlMg2,7Mn

Typical composition in %

Si <0,25
Fe <0,40
Cu <0,10
Mn 0,50-1,00
Mg 2,40-3,00
Cr 0,05-0,20
Zn <0,25
Be <0,0003
Ti 0,05-0,20
Others <0,05
Others, total <0,15

Classification

EN ISO 18273  :  S Al 5554 ( AlMg2,7Mn )
Matériel Nr  :  3.3538
AWS A 5-10  :  ER 5554

Base materials

See table

Remarks

This alloy was developed for applications at high temperatures and for resistance against intergranular corrosion. Joining of the base metal 5454 with alloys of the 6000 range is possible. The weld metal is sea water resistant. Consider the technological application reference.

Physical properties of pure weld metal (Approx. values)

0,2 % yield strength Rp0,2 [MPa]  :  100
Tensile strength Rm [MPa]  :  25
Elongation A5 ( L0=5d0 ) [%]  :  17
Test temperature [°C]  :  20

Welding position

PA, PB, PC, PF

Shielding gas

I1, I2, I3 (Argon, Helium or Argon/Helium-mixtures)

Polarity

MIG =+, WIG ~

Approvals

On request

Dimensions Ø

MIG-wires [mm]  :  0,8 ; 1,0 ; 1,2 ; 1,6 ; 2,0 ; 2,4
TIG-rods [mm]  :  1,6 ; 2,0 ; 2,4 ; 3,2 ; 4,0

Wire packagings

Spools  :  Packaging units

S 100 / 0,5 kg  :  20 spools = 10 kg (box)
S 200 / 2 kg  :  4 spools = 8 kg (box)
S 300 / 6 kg  :  84 spools = 504 kg (pallet)
B 300 / BS 300 / 7 kg  :  84 spools = 588 kg (pallet)
B 400 / 18 kg  :  28 spools = 504 kg (pallet)
B 400 / 40 kg  :  15 spools = 600 kg (pallet)
Fût / 80 kg  :  2 drums = 160 kg (pallet)
Fût Jumbo / 140 kg  :  2 drums = 280 kg (pallet)

Rod packagings

Carton 5 kg ; carton 10 kg  :  Length 1.000 mm