ML 5087 AlMg4,5MnZr

Typical composition in %

Si <0,25
Fe <0,40
Cu <0,05
Mn <0,70-1,10
Mg 4,50-5,20
Cr 0,05-0,25
Zn <0,25
Be <0,0003
Ti <0,15
Zr 0,10-0,20
Others <0,05
Others, total <0,15

Classification

EN ISO 18273  :  S Al 5087 (AlMg4,5 MnZr)
Matériel Nr  :  3.3546

Base materials

See table

Remarks

Zirconium micro alloyed. The weld is not susceptible to hot cracking. Particularly advantageous for complicated weldments involving clamp conditions. Consider the technological application reference.

Physical properties of pure weld metal (Approx. values)

0,2 % yield strength  :  125
Tensile strength Rm [MPa]  :  275
Elongation A5 ( L0=5d0 ) [%]  :  17
Test temperature [°C]  :  20

Welding position

PA, PB, PC, PF

Shielding gas

I1, I2, I3 (Argon, Helium or Argon/Helium-mixtures)

Polarity

MIG =+, WIG ~

Approvals

DNV-GL ; ABS ; DB ; TÜV ; Bureau Veritas

Dimensions Ø

MIG-wires [mm]  :  0,8 ; 1,0 ; 1,2 ; 1,6 ; 2,0 ; 2,4
TIG-rods [mm]  :  1,6 ; 2,0 ; 2,4 ; 3,2 ; 4,0

Wire packagings

Spools  :  Packaging units

S 100 / 0,5 kg  :  20 spools = 10 kg (box)
S 200 / 2 kg  :  4 spools = 8 kg (box)
S 300 / 6 kg  :  84 spools = 504 kg (pallet)
B 300 / BS 300 / 7 kg  :  84 spools = 588 kg (pallet)
B 400 / 18 kg  :  28 spools = 504 kg (pallet)
B 400 / 40 kg  :  15 spools = 600 kg (pallet)
Eco-drum / 80 kg  :  2 drums = 160 kg (pallet)
Jumbo-drum / 140 kg  :  2 drums = 280 kg (pallet)

Conditionnement baguettes TIG

Carton 5 kg ; carton 10 kg  :  Length 1.000 mm